Structures by: Baranets S.
Total: 11
Dibarium zinc diphosphide
Ba2P2Zn
Acta Crystallographica Section C (2020) 76, 9
a=6.756(4)Å b=13.108(8)Å c=6.385(4)Å
α=90° β=90° γ=90°
Niobium nickel arsenide
AsNb0.92Ni
Acta Crystallographica Section C (2018) 74, 5 623-627
a=6.2115(19)Å b=3.7150(11)Å c=7.172(2)Å
α=90° β=90° γ=90°
Niobium cobalt arsenide
AsCoNb
Acta Crystallographica Section C (2018) 74, 5 623-627
a=6.2656(15)Å b=3.7273(9)Å c=7.1589(17)Å
α=90° β=90° γ=90°
Niobium nickel germanide
GeNbNi
Acta Crystallographica Section C (2018) 74, 5 623-627
a=6.2989(8)Å b=3.7613(4)Å c=7.2033(8)Å
α=90° β=90° γ=90°
Al0.9Bi11Ca13.939Lu0.161
Al0.9Bi11Ca13.939Lu0.161
Journal of the American Chemical Society (2020)
a=16.9893(12)Å b=16.9893(12)Å c=22.6602(17)Å
α=90° β=90° γ=90°
Al0.889Bi11Ca13.949Lu0.163
Al0.889Bi11Ca13.949Lu0.163
Journal of the American Chemical Society (2020)
a=17.0092(12)Å b=17.0092(12)Å c=22.7001(17)Å
α=90° β=90° γ=90°
Al0.852Bi11Ca13.964Lu0.184
Al0.852Bi11Ca13.964Lu0.184
Journal of the American Chemical Society (2020)
a=17.0165(16)Å b=17.0165(16)Å c=22.730(2)Å
α=90° β=90° γ=90°
Al0.855Bi11Ca13.952Lu0.193
Al0.855Bi11Ca13.952Lu0.193
Journal of the American Chemical Society (2020)
a=17.026(2)Å b=17.026(2)Å c=22.735(3)Å
α=90° β=90° γ=90°
Al0.927Bi11Ca13.907Tm0.166
Al0.927Bi11Ca13.907Tm0.166
Journal of the American Chemical Society (2020)
a=17.019(2)Å b=17.019(2)Å c=22.714(3)Å
α=90° β=90° γ=90°
AlBi11Ca13.902La0.098
AlBi11Ca13.902La0.098
Journal of the American Chemical Society (2020)
a=17.029(2)Å b=17.029(2)Å c=22.689(3)Å
α=90° β=90° γ=90°
Al0.877Bi11Ca13.955Lu0.167
Al0.877Bi11Ca13.955Lu0.167
Journal of the American Chemical Society (2020)
a=17.0115(19)Å b=17.0115(19)Å c=22.696(3)Å
α=90° β=90° γ=90°